TECHNICAL SPECIFICATION
PRODUCT TYPE : EXPANDED POLYETHYLENE FOAM
PRODUCT DESCRIPTION : NORMAL (WHITE COLOR)/SPECIAL COLOR
: ANTI STATIC (PINK COLOR)/SPECIAL COLOR
PHYSICAL AND CHEMICAL SPECIFICATION
DIRECT EXTRUDE : 0.5 mm. – 13mm.
PHYSICAL APPEARANCE : SHEET / BAG / ROLL / BLOCK
Physical Properties |
Test Method |
Units |
FOAM |
1.4 |
1.7 |
2.0 |
2.2 |
3.2 |
6.0 |
Compressive Strength Vertical Direction |
ASTM D3575-93
Suffix D @ 25% / 50% |
psi |
6.5
15.0 |
7.5
16.5 |
8.5
17.0 |
9.0
18.5 |
10.0
20.0 |
25.0
50.0 |
Compression Set |
ASTM D3575-93
Suffix B |
% |
15.0 |
16.5 |
15.5 |
15.0 |
14.0 |
10.0 |
Tensile Strength |
ASTM D3575-93
Suffix T MD / CMD |
Psi |
33.0
21.0 |
35.0
24.0 |
38.0
27.0 |
40.0
30.0 |
45.0
35.0 |
72.0
52.0 |
Tear Resistance |
ASTM D3575-93
Suffix G MD / CMD |
lb/in |
10.0
7.0 |
11.0
8.0 |
12.0
9.5 |
13.0
11.0 |
16.0
13.0 |
23.0
19.0 |
Density Range |
ASTM D 3575 – 93 |
lb/ft2
kg/m3 |
1.4-1.6
22.4-25.6 |
1.6-1.9
25.6-30.4 |
1.9-2.1
30.4-33.6 |
2.1-2.4
33.6-38.4 |
2.5-3.2
38.4-51.2 |
5.8-6.2
51.2-99.2 |
Water Absorption |
ISO 2896 |
% |
< 0.1 |
< 0.1 |
< 0.1 |
< 0.1 |
< 0.1 |
< 0.1 |
Thermal Stability |
ASTM D3575 – 93
Suffix s |
% |
< 5 |
< 5 |
< 5 |
< 5 |
< 5 |
< 5 |
Contact Corrosivity
(Alum, Plate) |
Method 3005
FED STD, 101 |
|
None |
None |
None |
None |
None |
None |
Static Decay
(Anti-static Grade) |
EIA STD, 541
Appendix F |
sec |
< 2 sec |
Surface Resistivity
(Anti-static Grade) |
EIA STD, 541 |
BTU-IN |
1.0 x 109 - 1.0 x 1011 |
Thermal Conductivity
(k-Value) |
EIA STD,541 |
W/(m.k) |
0.030 – 0.040 |
Physical Stability (40/72hr.) |
EIA STD,541 |
|
- 0.7% |
Concentrated Ozone Stablility (50 pphm) |
EIA STD,541 |
|
Unbreakable |
Heat Distortion Temperature |
|
|
- 80o - 80o c |
CHEMICAL TYPE OF PRODUCT
NORMAL LOW-DENSITY POLYETHYLENE (LDPE)
TALC FOAMING AGENT
RIKEMAL AS-105 MASTER BATCH: NON-TOXIC FOR USU IN PLASTICS.
HDPE/LDPE Film Laminated Thickness 0.012-0.020 mm. (12-20 Micron).
ANTI- STATIC : THE ACTIVE ANTI STATIC AGENT MIGRATES TO THE POLYMER FILM SURFACE RESULTING IN AN ANTI-STATIC EFFECTS. THIS MASTERBATCH CONTAINS TWO KINDS OF ANTI ADDITIVES WITH SYNERGISTIC EFFECT TO GIVE A LONG-TERM ANTI STATIC EFFECT IN POLYMER PRODUCTS. FOR ANTI-STATIC TYPE 10 – 1011 OHMS / SQUARE METER
HEATER : HEATER INJECTION TEMPERATURE 112o C |